参考技術データ
Dowhon 標準コンパウンド | |||||||||||
HFM-50L (低硬度品) | HFM-Aシリーズ (圧縮成型向け) | HFM-Bシリーズ (インジェクション成型向け) | HFM-Fシリーズ (高フッ素含有タイプ) | ||||||||
HFM-50L | HFM-60A | HFM-70A | HFM-80A | HFM-90A | HFM-60B | HFM-70B | HFM-80B | HFM-60F | HFM-70F | HFM-80F | |
加硫特性MDR 170℃×10min | |||||||||||
ML (dNm) | 0.32 | 1.01 | 1.27 | 1.83 | 2.78 | 0.47 | 0.65 | 1.04 | 0.8 | 1.0 | 1.4 |
MH (dNm) | 8.76 | 15.33 | 18.75 | 25.47 | 34.91 | 11.37 | 13.41 | 19.52 | 11.8 | 15.7 | 19.9 |
ts2 (min) | 5.45 | 3.33 | 3.15 | 2.82 | 2.3 | 3.1 | 3.12 | 2.48 | 3.9 | 3.1 | 2.6 |
t10 (min) | 4.82 | 3.1 | 3.05 | 2.97 | 2.68 | 2.82 | 2.88 | 2.47 | 3.4 | 2.8 | 2.5 |
t50 (min) | 5.97 | 4.02 | 4.13 | 4.25 | 3.75 | 3.55 | 3.57 | 3.27 | 4.7 | 4.0 | 3.8 |
t90 (min) | 7.8 | 5.7 | 5.9 | 6.08 | 5.33 | 5.42 | 5.48 | 5.12 | 6.2 | 5.4 | 5.3 |
常態物性P/C:170℃×10min OC:230℃×24H | |||||||||||
強度 (Mpa) | 9.05 | 12.6 | 14.4 | 15.3 | 17 | 12.1 | 12.9 | 14.2 | 11.8 | 12.7 | 12.4 |
伸び (%) | 270 | 230 | 200 | 170 | 130 | 270 | 260 | 190 | 230 | 200 | 180 |
100%応力 (Mpa) | 1.57 | 3.25 | 5.19 | 8.43 | 13.6 | 2.78 | 3.93 | 6.65 | 2.8 | 4.9 | 6.5 |
硬度 1秒後 (Duro A) | 52 | 64 | 72 | 83 | 91 | 63 | 73 | 82 | 62 | 70 | 79 |
硬度 3秒後 (Duro A) | 50 | 62 | 70 | 81 | 90 | 62 | 71 | 81 | 60 | 68 | 77 |
比重 | 1.839 | 1.843 | 1.845 | 1.844 | 1.84 | 1.845 | 1.847 | 1.844 | 1.89 | 1.88 | 1.88 |
C/S (%)(200℃×72H) | 18 | 17 | 18 | 18 | 21 | 20 | 23 | 22 | 31 | 33 | 35 |
ムーニー粘度(ML1+10 121) | 30.9 | 55.1 | 62.5 | 75.1 | 96.6 | 38.3 | 43.3 | 55.7 | 49 | 55 | 62 |
参考技術データ
SOLVAYテクノフロン®使用 標準コンパウンド | |||||||||||
HSV-50L (低硬度品) | HSV-Aシリーズ (圧縮成型向け) | HSV-Bシリーズ (インジェクション成型向け) | HSV-Fシリーズ (高フッ素含有タイプ) | ||||||||
HSV-50L | HSV-60A | HSV-70A | HSV-80A | HSV-90A | HSV-60B | HSV-70B | HSV-80B | HSV-60F | HSV-70F | HSV-80F | |
加硫特性MDR 170℃×10min | |||||||||||
ML (dNm) | 0.5 | 1.4 | 1.9 | 2.5 | 3.5 | 0.6 | 0.8 | 1.2 | 0.7 | 0.9 | 1.2 |
MH (dNm) | 8.7 | 11.7 | 15.8 | 21.2 | 28.9 | 11.7 | 15.0 | 19.9 | 12.2 | 16.8 | 22.5 |
ts2 (min) | 4.6 | 2.9 | 2.6 | 2.3 | 2.1 | 3.8 | 3.4 | 3.3 | 5.3 | 4.2 | 3.2 |
t10 (min) | 3.9 | 2.5 | 2.3 | 2.2 | 2.3 | 3.5 | 3.2 | 3.3 | 5.0 | 4.1 | 3.3 |
t50 (min) | 5.2 | 3.3 | 3.3 | 3.4 | 3.9 | 4.4 | 4.2 | 4.7 | 6.1 | 5.1 | 4.2 |
t90 (min) | 7.2 | 4.8 | 5.2 | 5.1 | 5.8 | 6.3 | 6.2 | 6.8 | 7.3 | 6.4 | 5.6 |
常態物性P/C:170℃×10min OC:230℃×24H | |||||||||||
強度 (Mpa) | 9.1 | 10.8 | 13.4 | 15.3 | 16.4 | 11.7 | 15.5 | 15.9 | 12.0 | 13.4 | 14.5 |
伸び (%) | 310 | 280 | 230 | 190 | 150 | 240 | 230 | 180 | 260 | 220 | 200 |
100%応力 (Mpa) | 1.4 | 2.6 | 5.0 | 7.5 | 11.4 | 2.82 | 5.04 | 7.65 | 2.7 | 4.9 | 6.7 |
硬度 1秒後 (Duro A) | 51 | 60 | 70 | 80 | 89 | 63 | 72 | 83 | 63 | 72 | 83 |
硬度 3秒後 (Duro A) | 49 | 58 | 68 | 78 | 87 | 61 | 70 | 81 | 61 | 70 | 81 |
比重 | 1.83 | 1.84 | 1.84 | 1.84 | 1.84 | 1.84 | 1.84 | 1.84 | 1.90 | 1.89 | 1.89 |
C/S (%)(200℃×72H) | 18 | 17 | 16 | 18 | 16 | 14 | 14 | 15 | 32 | 30 | 32 |
ムーニー粘度 (ML1+10 121) | 32 | 68 | 80 | 95 | 117 | 37.1 | 42.3 | 52.2 | 60 | 64 | 72 |
|ケマーズ社 Viton™(バイトン™) |スリーエムジャパン
これからの株式会社北栄
3Mフッ素ゴム以外の混練り事業を展開することが可能となり、今後はより他製品の取り扱いを拡販し、お客様のご希望に柔軟に対応することが出来ます。
また、お客様とも直接お話しをさせて頂くことでスピーディーな生産を行い、より多くのお客様に株式会社北栄を知って頂けるよう日々精進してまいります。
1.人間生活への貢献
当社は社会の発展と共に、
より良い製品を社会に提供する事により豊かな人間生活へ貢献できるように努める。
より良い製品を社会に提供する事により豊かな人間生活へ貢献できるように努める。
2.人間成形への人材育成
当社は当社に属するもの人間社会での協調性を重視し団体作業の重要性を認識させ
人材育成に努める。
人材育成に努める。
3.経営基盤の向上及び維持
当社は、安定した経営基盤を維持強化するため積極的に利益を追求し、健全経営に努める。
これまで築き上げてきた技術とノウハウを最大限に生かしお客様に安定した製品をお届けいたします。
4.顧客満足
弊社は、他社様での対応が出来ないなど実現が難しい製品なども、積極的にお客様と直接ご相談をさせて頂き
実現を可能に出来る様お手伝いをさせて頂きます。
また、お客様のご要望に合わせ少量数量や最短納期で対応させていただきます。
また、お客様のご要望に合わせ少量数量や最短納期で対応させていただきます。
5.安全第一をモットーとして徹底した品質管理
3Mフッ素ゴムの混練り協力会社として30年以上にわたり事故無く混練製造をしてきた実績がございます。
環境問題の課題と共により良いフッ素ゴム混練製造の両立ができる会社作りを目標として精進してまいります。
2004年に取得したISO9001をもとに品質管理の徹底を行っております。
環境問題の課題と共により良いフッ素ゴム混練製造の両立ができる会社作りを目標として精進してまいります。
2004年に取得したISO9001をもとに品質管理の徹底を行っております。
また、お客様指定ポリマーでの製造や物性条件のご相談も弊社にてご対応させて頂きます。